Acrylic binder for non woven coating

RF-9402 Textile Emulsion

RF-9402 is a stable water-based styrene acrylic copolymer emulsion. It is a special molding glue developed by our company.

RF-9402 is suitable for the interior blankets of all kinds of automotive, all kinds of thickness non-woven fabrics, needle-punched

carpet, non-woven fabrics adhesion, sofa fabric, and so on.

• Three coating processes: dip coating, spray coating, foaming coating

• Good permeability and adhesion to various synthetic fibers

• Stiffness

• Improve the stiffness hand feeling of the coated fabric

• Good resilience

• Resistance to yellowing

• Eco-friendly, low odor, low VOC

• Mixed with our company’s similar products can make the fabric have the different stiffness of hand feeling.

Appearance

Milky White With Blue Shade

Solid Content, wt% 44.0 ± 1

pH 6.0 - 8.0

Glass Transition Temperature (Tg) 45 °C

Viscosity (Brookfield LV, spindle 1@60 rpm, 25°C) < 100 cps

Ionicity Anionic

Before using, adjust the expansion ratio according to the requirements of the desired amount of spread and hardness. Add a suitable amount of foaming agent, cross-linking agent, or thickener based on an actual situation. After the coating is applied, please heat for 2-3 minutes at a high temperature of 160-180°C.

RF-9406 Textile Emulsion

RF-9406 is a stable water-based styrene acrylic copolymer emulsion. It is a special molding glue developed by our company.

RF-9406 is suitable for the interior blankets of all kinds of automotive, all kinds of thickness non-woven fabrics, needle-punched

carpet, non-woven fabrics adhesion, sofa fabric, and so on.
• Three coating processes: dip coating, spray coating, foaming

coating

• Good permeability and adhesion to various synthetic fibers

• Moderate stiffness

• Improve the moderate stiffness hand feeling of the coated fabric

• Good resilience

• Resistance to yellowing

• Eco-friendly, low odor, low VOC

• Mixed with our company’s similar products can make the fab

ric have the different stiffness of hand feeling.

Appearance

Milky White With Blue Shade

Solid Content, wt% 45.0 ± 1

pH 6.0 - 8.0

Glass Transition Temperature (Tg) 30 °C

Viscosity (Brookfield LV, spindle 2@30 rpm, 25°C) < 200 cps

Ionicity Anionic