--Defoamer dispersibility in water: Under stirring, 90 g of process water was slowly added to a beaker containing 10 g of defoamer, and gently shaken to observe its dispersion in water (excellent: rapid diffusion; medium: most of the dispersion was slow, and a small amount of flocculent The material is more difficult to disperse; poor: not easy to disperse, and the floc is difficult to disappear, the cup wall has oil).
-- High temperature resistance (high temperature and high pressure cooking test). Take a certain amount of defoamer YAT722 in a beaker, dilute it evenly with about 4 times of water, and cook in a pressure cooker. When the temperature rises to 130 °C, start timing, cook at constant temperature and constant pressure for 2 hours, cool down to room temperature. The sample was taken out to observe the high temperature and high pressure resistance (130±2 ° C, 2 h) performance and the presence or absence of delamination and oil droplets drifting out.
--Shear resistance (high shear resistance test). 100 mL of the sample was taken, diluted with water to 500 mL with stirring, heated to 85 ° C and 95 ° C, respectively, and sheared at 3000 rpm for 1 hr under a high speed shearing machine to stop shearing, and the oily condition was observed.
--Electrolyte resistance, acid and alkali resistance, compatibility and viscosity, etc., can be contracted according to the actual application process and applicable environment of the customer.
Amber Zhang Ms.
Foreign trade
Zhejiang Ruico Advanced Materials Co., Ltd. (Stock No.873233)
Add: No.188, Liangshan Road, Linghu Town, Nanxun District, Huzhou City, Zhejiang Province, China 313018
Phone: +86 (572) 2903236
Fax: +86 (572) 2905222
Wechat: 15534631339
Website: www.ruicoglobal.com
Email: [email protected]